Recently, many customers inquired whether high chromium wear parts could use TM52 steel bonded TiC cermets inserts . As our experience, it is not recommended.

Our TiC cermets inserts has the similar thermal expansion coefficient as base material:13% high manganese steel . When the surface of tic rods be melted, two materials will be bonded together perfectly. There is no need to worry about the problem of “drop out “.

And this properity is not working for high chromium wear part.

Basing on this, we do not recommend.